Display device and method of manufacturing the same

ABSTRACT

Thin film transistors are formed over an insulation substrate which constitutes a display device. Each thin film transistor includes a semiconductor layer made of polysilicon which is comprised of a channel region, drain and source regions which are arranged at both sides of the channel region and are doped with impurity of high concentration, and an LDD region which is arranged at least either between the drain region and the channel region or between the source region and the channel region and are doped with impurity of low concentration, an insulation film which is formed over an upper surface of the semiconductor layer and respectively sequentially decreases a film thickness thereof in a step-like manner as the insulation film is extended to the channel region, the LDD region, the drain and the source regions, and a gate electrode which is formed over the channel region through the insulation film. The display device having such a constitution can enhance the numerical aperture and can suppress the magnitude of stepped portions in a periphery of the thin film transistor.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to a display device, and more particularly, to an active matrix type display device and a fabricating method thereof.

[0003] 2. Description of the Related Art

[0004] In a liquid crystal display device which is known as a typical example of this kind of display device, on a liquid-crystal-side surface of one of transparent substrates which are arranged to face each other in an opposed manner through liquid crystal, gate signal lines which are extended in the x direction and are arranged in parallel in the y direction and drain signal lines which are extended in the y direction and are arranged in parallel in the x direction are formed and respective regions surrounded by these signal lines define pixel regions.

[0005] On each pixel region, at least, a thin film transistor which is operated in response to scanning signals from one-side gate signal line and a pixel electrode to which video signals are supplied from one-side drain signal line through the thin film transistor are formed.

[0006] The pixel electrode generates an electric field between the pixel electrode and a counter electrode thus controlling the light transmittivity of the liquid crystal.

[0007] Further, as the thin film transistor, there has been a transistor which uses a semiconductor layer which is referred to as a so-called a low-temperature polysilicon (p-Si).

[0008] Such a thin film transistor can be formed by a low temperature process at a temperature of not more than approximately 450° C.

[0009] Then, also there has been known a liquid crystal display device in which a scanning driving circuit which supplies scanning signals to the gate signal lines and a video driving circuit which supplies video signals to the drain signal lines are formed on one of the above-mentioned substrates.

[0010] Each driving circuit is comprised of a large number of complementary MIS transistors. It is because that these MIS transistors can be formed along with the formation of the above-mentioned thin film transistors.

[0011] As the constitution of such thin film transistors, the constitution which is disclosed in Japanese Laid-open Patent Publication 163366/1999 has been known, for example.

[0012] With respect to the thin film transistor having such a constitution, so-called LDD (Lightly Doped Drain) regions are formed respectively between a channel region thereof and drain and source regions which are formed at both sides of the channel region and the widths of respective LDD regions are made uniform so as to make the magnitude of ON currents uniform.

[0013] These LDD regions are regions which are doped with impurity having the concentration lower than the concentration of impurity doped into the drain and source regions. The LDD regions are formed to alleviate the concentration of an electric field at these portions.

[0014] However, with respect to such a thin film transistor, no consideration has been paid to a film thickness of an insulation film (functioning as a gate insulation film) which covers a channel region, an LDD region and drain and source regions thereof. Accordingly, it has been pointed out that the areas of the tapered surfaces of contact holes cannot be reduced so that the numerical aperture cannot be enhanced or there arises a defect with respect to the coating ability of an interlayer insulation film due to the formation of a stepped portion in the periphery of a gate electrode of the thin film transistor.

[0015] The present invention has been made in view of such circumstances and it is an object of the present invention to provide a display device which can enhance the numerical aperture and can resolve defects which occur in a periphery of a gate electrode of a thin film transistor.

[0016] Further, it is another object of the present invention to provide a method for fabricating a display device which can reduce a voltage necessary for the ion implantation of impurity at the time of forming the thin film transistors.

SUMMARY OF THE INVENTION

[0017] To briefly explain the summary of inventions which constitute typical examples of inventions described in this specification, they are as follows.

[0018] That is, a display device according to the present invention is characterized in that, for example, a thin film transistor is formed over at least one of respective substrates which are arranged to face each other in an opposed manner sandwiching liquid crystal therebetween, and the thin film transistor includes a semiconductor layer made of polysilicon which is comprised of a channel region, drain and source regions which are arranged at both sides of the channel region and are doped with impurity of high concentration, and at least an LDD region which is arranged between the drain region and the channel region and between source region and the channel region or between the drain region and the channel region and are doped with impurity of low concentration, an insulation film which is formed over an upper surface of the semiconductor layer and respectively sequentially decreases a film thickness thereof in a step-like manner as the insulation film is extended to the channel region, the LDD region, the drain and the source region or the drain region, and a gate electrode which is formed over the channel region through the insulation film.

[0019] In the display device having such a constitution, the film thickness of the insulation film on the drain and source regions can be made extremely smaller than the film thickness of the insulation film on the channel region.

[0020] Accordingly, the tapered areas in the contact holes of the insulation film which are formed for drain and source electrodes can be reduced so that the areas of the respective electrodes can be reduced. Accordingly, the numerical aperture can be enhanced.

[0021] Further, since the insulation film can be made by stepped portions thereof divided in two stages in the course of reaching the drain and source regions from the channel region, the substantially smooth oblique surfaces can be formed so that the drawbacks derived from the stepped portions can be resolved.

[0022] Further, a method for fabricating a display device according to the present invention is characterized in that, for example, a thin film transistor is formed over an insulation substrate, and the thin film transistor is formed through following steps comprising a step in which a semiconductor layer made of polysilicon, an insulation film and a conductive layer are formed over the substrate side, a step which makes the conductive film remained on a channel region and an LDD region and performs the ion plantation of impurity of high concentration using the remaining conductive layer as a mask, and a step which makes the conductive film remained on the channel region and performs the ion plantation of impurity of low concentration using the remaining conductive layer as a mask, and a resist film which is used for patterning the conductive layer to be remained on the channel region is formed of a portion obtained by removing a periphery of the resist film which is used for patterning the conductive layer remained on the channel region and the LDD region, and at the time of making the conductive film remained on the channel region and the LDD region and further on the channel region, by using the conductive film as a mask, a surface of the insulation film which is exposed from the mask is slightly etched.

[0023] In the method for fabricating the display device having such a constitution, at the time of performing the ion implantation of the impurity of high concentration and the ion implantation of the impurity of low concentration respectively, a film thickness of the insulation film which constitutes a through film is made smaller than a film thickness of the insulation film formed over the channel region and hence, a voltage necessary for the ion implantation can be reduced so that damages on the insulation film can be minimized.

BRIEF DESCRIPTION OF THE DRAWINGS

[0024]FIG. 1 is a constitutional view showing one example of a thin film transistor of a display device according to the present invention and is a cross-sectional view taken along a line I-I of FIG. 3;

[0025]FIG. 2 is a schematic plan view showing one example of the display device according to the present invention;

[0026]FIG. 3 is a plan view showing one example of a pixel of the display device according to the present invention;

[0027]FIG. 4A to FIG. 4E are process flow views showing one embodiment of a method for fabricating a display device according to the present invention;

[0028]FIG. 5A to FIG. 5D are process flow views showing another embodiment of a method for fabricating a display device according to the present invention;

[0029]FIG. 6A to FIG. 6F are process flow views showing another embodiment of a method for fabricating a display device according to the present invention;

[0030]FIG. 7 is an explanatory view showing a pattern of a gate electrode of a thin film transistor manufactured by a step shown in FIG. 5A to FIG. 5D;

[0031]FIG. 8A to FIG. 8D are process flow views showing another embodiment of a method for fabricating a display device according to the present invention;

[0032]FIG. 9A and FIG. 9B are process flow views showing another embodiment of a method for fabricating a display device according to the present invention;

[0033]FIG. 10A and FIG. 10B are process flow views showing another embodiment of a method for fabricating a display device according to the present invention;

[0034]FIG. 11 is a process flow view showing another embodiment of a method for fabricating a display device according to the present invention; and

[0035]FIG. 12A to FIG. 12G are process flow views showing another embodiment of a method for fabricating a display device according to the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0036] Embodiments of a display device according to the present invention are explained hereinafter in conjunction with drawings.

[0037] [Overall Constitutional View]

[0038]FIG. 2 is an overall constitutional view showing one embodiment of a liquid crystal display device which constitutes one example of the display device according to the present invention.

[0039] In the drawing, first of all, the liquid crystal display device is provided with a transparent substrate SUB1 and the transparent substrate SUB1 is arranged to face a transparent substrate SUB2 in an opposed manner while sandwiching liquid crystal therebetween.

[0040] The transparent substrate SUB2 is formed while having an area slightly smaller than the area of the transparent substrate SUB1 and has a lower-side surface thereof in the drawing made coplanar with a lower-side surface of the transparent substrate SUB1 in the drawing. Accordingly, with respect to other peripheral portions excluding the lower side in the drawing, there exist regions where the transparent substrate SUB2 is not formed.

[0041] On the liquid-crystal-side surface of the transparent substrate SUB1 at this region, a scanning driving circuit V and a video driving circuit He which will be explained later are formed.

[0042] On the liquid-crystal-side surface of the transparent substrate SUB1, gate signal lines GL which are extended in the x direction in the drawing and are arranged in parallel in the y direction in the drawing are formed, wherein one ends (disposed at the left side in the drawing) of the gate signal lines GL are connected to the scanning driving circuit V. Further, also on the liquid-crystal-side surface of the transparent substrate SUB1, drain signal lines DL which are extended in the y direction in the drawing and are arranged in parallel in the x direction in the drawing are formed, wherein one ends (disposed at the upper side in the drawing) of the drain signal lines DL are connected to the video driving circuit He.

[0043] Respective regions surrounded by respective gate signal lines GL and respective drain signal lines DL define pixel regions. Each pixel region is provided with a thin film transistor TFT which is operated in response to scanning signals supplied from one-side gate signal line GL and a pixel electrode PX to which video signals are supplied from one-side drain signal line DL through the thin film transistor TFT.

[0044] The pixel electrode PX generates an electric field between the pixel electrode PX and a counter electrode CT which is formed in common with respective pixel regions on the liquid-crystal-side surface of the transparent substrate SUB2 thus controlling the light transmittivity of the liquid crystal by to this electric field.

[0045] Here, with respect to the thin film transistor TFT, a semiconductor layer thereof is formed of so-called low-temperature polysilicon, for example.

[0046] Further, the scanning driving circuit V and the video driving circuit He are respectively comprised of a large number of transistors which have substantially the same constitution as the above-mentioned thin film transistors TFT.

[0047] These respective transistors also adopt low-temperature polysilicon as the material of the semiconductor layer and are formed along with the formation of the thin film transistor TFT.

[0048] Here, the transparent substrate SUB2 is fixedly secured to the transparent substrate SUB1 by a sealing member SL which also performs the sealing of the liquid crystal between the transparent substrates SUB1 and SUB2.

[0049] [Constitution of Pixel]

[0050]FIG. 3 is a plan view for showing one embodiment of the constitution of one pixel region out of respective pixel regions. Further, FIG. 1 is a cross-sectional view taken along a line I-I of FIG. 3.

[0051] On the liquid-crystal-side surface of the transparent substrate SUB1, first of all, a semiconductor layer AS made of polysilicon is formed.

[0052] This semiconductor layer AS is a semiconductor layer which constitutes a thin film transistor TFT. The semiconductor layer AS is formed in an L-shaped pattern, for example, in the drawing.

[0053] The semiconductor layer AS has one end portion thereof positioned in the inside of the pixel region surrounded by the gate signal lines GL and the drain signal lines DL which will be explained later. Further, the semiconductor layer AS has the other end portion thereof superposed on the drain signal line DL. Respective end portions of the semiconductor layer AS are formed to ensure a relatively large area thus constituting contact portions.

[0054] An insulation film GI made of SiO₂ is, for example, formed over the surface of the transparent substrate SUB1 such that the insulation film GI also covers the semiconductor layer AS (see FIG. 1). The insulation film GI mainly functions as a gate insulation film of the thin film transistor TFT and hence, a film thickness thereof is set to a suitable value (approximately 100 nm) as an insulation film.

[0055] Further, the gate signal lines GL which are extended in the x direction and are arranged in parallel in the y direction in the drawing are formed over the surface of the insulation film GI.

[0056] The gate signal line GL has an extension portion which is formed such that the extension portion intersects and sits astride a portion of the semiconductor layer AS except for both ends of the semiconductor layer AS at a position in the vicinity of the thin film transistor TFT. The extension portion functions as a gate electrode GT of the thin film transistor TFT.

[0057] In this embodiment, for example, Mo, Mo alloy (MoW, MoCr), Ti, Ti alloy (Tiw) can be used as material for the gate electrode GT (gate signal line GL).

[0058] A capacitance signal line CL which runs parallel to the gate signal lines GL is formed between the respective gate signal lines GL. The capacitance signal line CL is, for example, formed simultaneously with the formation of the gate signal lines GL. Accordingly, the capacitance signal line CL is made of the same material as the gate signal lines GL.

[0059] A first interlayer insulation film LGI1 made of SiO₂, for example, is formed over the surface of the transparent substrate SUB1 such that the first interlayer insulation film LGI1 also covers the gate signal lines GL and the capacitance signal line CL (see FIG. 1).

[0060] Contact holes CH1, CH2 are formed in the first interlayer insulation film LGI1, wherein the contact hole CHI makes a portion of a source region SD1 (region disposed at a side which is connected to the pixel electrode PX which will be explained later) of the thin film transistor TFT exposed, and the contact hole CH2 makes a portion of a drain region SD2 (region disposed at a side which is connected to the drain signal line DL which will be explained later) of the thin film transistor TFT exposed.

[0061] On an upper surface of the first interlayer insulation film LGI1, the drain signal lines DL which are extended in the y direction and are arranged in parallel in the x direction in the drawing are formed. The drain signal line DL is formed such that the drain signal line DL is connected to the drain electrode SD2 of the thin film transistor TFT at a portion of the contact hole CH2.

[0062] Further, at the time of forming the drain signal lines DL, the source electrode SD1 of the thin film transistor TFT is formed at a portion of the contact hole CH1.

[0063] Then, on a surface of the transparent substrate SUB1, a second interlayer insulation film LGI2 made of SiN, for example, is formed such that the second interlayer insulation film LGI2 also covers the drain signal lines DL and the source electrode SD1. A contact hole CH3 is formed in the second interlayer insulation film LGI2. The contact hole CH3 makes a portion of the source electrode SD1 of the thin film transistor TFT exposed.

[0064] Further, on an upper surface of the second interlayer insulation film LGI2, the pixel electrode PX made of ITO (Indium-Tin-Oxide), for example, is formed.

[0065] The pixel electrode PX is formed such that the pixel electrode PX is disposed adjacent to the gate signal lines GL and the drain signal lines DL and occupies a major portion of the pixel region.

[0066] In the above-mentioned embodiment, gate electrode GT is integrally formed with the gate signal line GL. However, it is needless to say that the gate signal line GL can be made of material different from material of the gate electrode GT and they may be electrically connected to each other.

[0067] [Thin Film Transistor TFT]

[0068]FIG. 1 is a constitutional view showing one embodiment of the thin film transistor TFT and also is a cross-sectional view taken along a line I-I of FIG. 3.

[0069] The thin film transistor TFT has the semiconductor layer AS thereof made of polysilicon.

[0070] Here, the semiconductor layer AS is formed of an i-type layer (intrinsic layer: layer which is not doped with conductive impurity) which is disposed right below the gate electrode GT, layers doped with an n-type impurity of relatively low concentration which are disposed at both sides of the i-type layer, and layers doped with an n-type impurity of relatively high concentration which are disposed at both sides of the layers doped with the n-type impurity of relatively low concentration.

[0071] The i-type semiconductor layer AS functions as the channel region of the thin film transistor TFT and the layers doped with the n-type impurity of relatively high concentration respectively function as a drain region (region at a side which is connected to the drain signal line DL) and a source region (region at a side which is connected to the pixel electrode PX).

[0072] Further, the layers AS₀ doped with the n-type impurity of relatively low concentration function as layers which prevent a so-called drain avalanche hot carrier (DAHC) and are referred to as LDD (Lightly Doped Drain) regions. In these LDD regions, the electric field is alleviated thus preventing the concentration of an electric current whereby the reliability of the thin film transistor TFT can be enhanced.

[0073] Due to such a constitution, in this embodiment, the width L of the layer AS₀ extending from the channel region to the drain region and the width L of the layer AS₀ extending from the channel region to the source region are set to the same and accurate value.

[0074] That is, when the width L is set to an excessively large value, the resistance of the semiconductor layer AS is increased, while when the width L is set to an excessively small value, the concentration of the electric field occurs.

[0075] Further, a film thickness of the insulation film GI which covers the semiconductor layer AS is set to approximately 100 nm (preferably not more than 100 nm) right above the channel region, not more than 90 nm right above the layers AS₀ which are doped with the n-type impurity having the small concentration, and not more than 80 nm, more preferably not more than 60 nm right above the drain region and the source region.

[0076] In other words, the insulation film GI is configured to make the film thickness thereof reduced in a step-like manner in the order of the portion thereof right above the channel region, the portion thereof right above the layers AS₀ which are doped with the n-type impurity having the small concentration, and the portions thereof right above the drain region and the source region respectively.

[0077] Due to such a constitution, the film thickness of the insulation film GI right above the drain region and the source region becomes thinner than the film thickness of the insulation film GI right above the channel region by not less than 20 nm, and more preferably not less than 40 nm.

[0078] This implies that the increase of areas occupied by tapers on the inner surfaces of the contact holes CH1, CH2 which are respectively formed in the drain region and the source region for forming electrodes can be prevented. Accordingly, an advantageous effect that the numerical aperture of the pixel can be enhanced is obtained.

[0079] This advantageous effect becomes more apparent by setting the difference between the film thickness of the insulation film GI right above the layers AS₀ which are doped with the n-type impurity having the small concentration and the film thickness of the insulation film GI right above the drain and source regions larger than the difference between the film thickness of the insulation film right above the channel region and a film thickness of the insulation film right above the layers AS₀ which are doped with the n-type impurity having the small concentration.

[0080] Further, with the provision of the insulation film GI having such a constitution, the stepped portions formed in the vicinity of the gate electrode GT are divided in two stages so that each step of each stepped portion becomes small whereby an advantageous effect that a coverage of the interlayer insulation films LGI1, LGI2 can be enhanced is obtained.

[0081] Still further, this implies that the insulation films LGI1, LGI2 can be formed relatively flat. Accordingly, an advantageous effect that the disconnection of the signal lines or electrodes formed over respective interlayer insulation films LGI1, LGI2 which occurs due to the presence of the steps can be obviated is obtained.

[0082] Here, in this embodiment, although the film thickness of the insulation film GI right above the channel region is set to not more than 100 nm, the film thickness of the insulation film GI right above the layers AS₀ which are doped with the n-type impurity having the small concentration is set to not more than 90 nm, and the film thickness of the insulation film GI right above the drain region and the source region is set to not more than 60 nm, it is needless to say that these film thicknesses may be respectively set to not more than 80 nm, not more than 70 nm, and not more than 40 nm.

[0083] [Method for Fabricating Thin Film Transistor]

[0084] One example of a method for fabricating thin film transistor is explained in conjunction with FIG. 4A to FIG. 4E.

[0085] Step 1. (FIG. 4A)

[0086] On the liquid-crystal-side surface of the transparent substrate SUB1, the semiconductor layer AS made of polysilicon, (p-Si), an insulation film made of Si0 ₂, for example, and a metal layer made of Cr or the like, for example are laminated sequentially.

[0087] Here, the insulation film is formed of material which functions as the gate insulation film GI and the metal layer is formed of material which functions as the gate electrode GT.

[0088] Further, although the insulation film having a relatively thick film thickness is formed, it is preferable to set the film thickness to not more than 100 nm. This is because that the semiconductor layer AS made of p-Si is formed as a layer below the insulation film and a thermal oxidation film having a favorable quality such as single-crystal silicon cannot be formed so that only the insulation film which can be formed at a low temperature can be formed whereby it is difficult to make the film thickness thin due to the characteristics of the insulation film.

[0089] Then, a photo resist film RE is formed over a surface of the metal layer by coating, for example.

[0090] Step 2. (FIG. 4B)

[0091] The photo resist film RE is selectively exposed using a photo mask MK.

[0092] Light shielding films mk are formed over regions of the photo mask MK which correspond to the channel region and portions disposed at both sides of the channel region of the thin film transistor TFT.

[0093] In this case, the light shielding film mk₀ which corresponds to the channel region of the thin film transistor TFT is formed such that the light shielding film mk₀ completely shields the light and the light shielding films mk₁ which are disposed at both sides of the light shielding film mk₀ are formed in a mesh form, for example, so as to partially shield the light (hereinafter, such an exposure is referred to as “half exposure” for the convenience sake).

[0094] Here, the light shielding films mk₁ are portions which correspond to respective LDD regions formed over the semiconductor layer AS and are formed to have the width equal to the width of respective LDD regions.

[0095] By developing the photo resist film RE which is exposed using such a photo mask MK, the photo resist film RE remains on the channel region and the regions which are disposed at both sides of the thin film transistor TFT, while the photo resist film RE is removed on other regions.

[0096] In this case, the remaining photo resist film RE exhibits the thick film thickness on the channel region and the thin film thickness on the regions corresponding to both sides of the channel region.

[0097] Step 3. (FIG. 4C)

[0098] Using the remaining photo resist film RE as a mask, the metal layer exposed from the mask is selectively etched so that the insulation film GI is exposed.

[0099] In this case, the surface of the insulation film GL is slightly etched so that the film thickness of the exposed insulation film GI becomes slightly smaller than the film thickness of the insulation film GI below the mask.

[0100] Further, the ion implantation of the n-type impurity of high concentration is performed with the mask remained. Due to such an ion implantation, the ion of high concentration is implanted into the semiconductor layer AS below the insulation film at regions other than regions where the mask is formed so that the drain and source regions are formed.

[0101] Here, since the insulation film GI which functions as a through film for ions at the time of the ion implantation has a film thickness of not more than 100 nm, the acceleration voltage for the ion implantation can be lowered. Accordingly, the damage which the insulation film GI receives as the through film can be suppressed as small as possible whereby the subsequent activation can be performed easily.

[0102] Step 4. (FIG. 4D)

[0103] By ashing the remaining photo resist film RE, the surface thereof is removed while remaining a portion thereof. That is, the ashing process is performed until the photo resist film RE having a large film thickness remains on the channel region and the photo resist film RE having a small film thickness formed at both sides of the photo resist film RE having a large film thickness are removed.

[0104] Step 5. (FIG. 4E)

[0105] Using the remaining photo resist film RE as a mask, the metal layer exposed from the mask is etched so that the gate electrode GT is formed and, at the same time, the insulation film GI at both sides of the channel region is exposed.

[0106] In this case, the surface of the insulation film GI is slightly etched and the film thickness of the exposed insulation film GI is made smaller than the film thickness of the insulation film GI below the mask. In this case, the insulation film GI on the drain and source regions has the surface thereof also slightly etched in the same manner.

[0107] Further, the ion implantation of the n-type impurity of low concentration is performed with the mask remained. Due to such an ion implantation, the ion of low concentration is implanted into the semiconductor layer below the insulation film at regions other than regions where the mask is formed so that the LDD regions are formed.

[0108] Here, since the insulation film GI which functions as a through film for ions at the time of the ion implantation has a film thickness of not more than 100 nm, the acceleration voltage for the ion implantation can be lowered. Accordingly, the damage which the insulation film GI receives as the through film can be suppressed as small as possible whereby the subsequent activation can be performed easily.

[0109] [Other Fabricating Method]

[0110]FIG. 5A to FIG. 5D are process flow views showing another embodiment of the fabricating method of thin film transistors shown in FIG. 4A to FIG. 4E.

[0111] In the drawings, steps of this fabricating method are the same as those of the fabricating method shown in FIG. 4A to FIG. 4E except for the formation of the photo resist film RE which is used at the time of forming the metal layer which is used as the gate electrode GT.

[0112] As shown in FIG. 5B, first of all, although the metal layer is made to remain on the channel region and the portions disposed at both sides of the channel region of the thin film transistor TFT, the photo resist film RE which works as the mask is formed as a film having the uniform thickness.

[0113] With respect to the photo resist film RE which is made to remain in this manner, the metal layer exposed from the photo resist film RE is etched and the semiconductor layer AS is doped with the n-type impurity of high concentration so that the drain and the source regions are formed.

[0114] Then, using the photo resist film RE as a mask, the metal film which is exposed from the mask is etched and, thereafter, the photo resist film RE is subjected to an ashing process.

[0115] Accordingly, the photo resist film RE is made to remain on the channel region, while the photo resist film RE is removed at the portions disposed at both sides of the channel region. In this case, the remaining photo resist film RE exhibits a pattern indicated by a solid line in FIG. 7 (the pattern being similar to a pattern of the gate electrode GT). In FIG. 7, a pattern indicated by a dotted line is a pattern before the photo resist film is subjected to the ashing process. In this manner, the gate electrode GT of the thin film transistor TFT formed according to this embodiment is eventually formed in a round shape at end thereof.

[0116] With respect to the photo resist film RE which is made to remain in this manner, the metal layer which is exposed from the photo resist film RE is etched and the semiconductor layer AS is doped with the n-type impurity of low concentration.

[0117] [Fabricating Method of Complementary Thin Film Transistor]

[0118] The thin film transistor TFT in the above-mentioned embodiment refers to the thin film transistor TFT formed in the pixel region.

[0119] However, the scanning driving circuit V or the video driving circuit He which is formed in the periphery of the liquid crystal display part as shown in FIG. 2 is also formed of a large number of thin film transistors TFT. Accordingly, it is needless to say that the present invention is also applicable to these thin film transistors TFT.

[0120] In this case, as the thin film transistors TFT which form each driving circuit, the thin film transistors of a complementary type consisting of a p-channel type transistor and an n-channel type transistor are popularly used and hence, one embodiment of the fabricating method of the complementary type thin film transistors TFT is explained in conjunction with FIG. 6A to FIG. 6F.

[0121] Step 1. (FIG. 6A)

[0122] First of all, since it is unnecessary for the p-type thin film transistor TFT which constitutes one of complementary type thin film transistors TFT which are arranged adjacent to each other to form the LDD regions, after forming the gate electrode, the p-type impurity of high concentration is implanted into the semiconductor layer AS using the gate electrode as a mask.

[0123] In this case, the region where n-type thin film transistor TFT is formed is a region which is formed by sequentially laminating the semiconductor layer AS made of polysilicon, the insulation film GI and the metal layer GT from the substrate SUB1 side.

[0124] Step 2. (FIG. 6B)

[0125] The photo resist film RE is formed over the entire surface of the transparent substrate SUB1 by coating, for example.

[0126] Step 3. (FIG. 6C)

[0127] The photo resist film RE is selectively exposed using the photo mask.

[0128] In this case, the whole area of the region where the p-type thin film transistor TFT is formed is fully shielded from light such that the photo resist film remains on the whole area of the region where the p-type thin film transistor TFT is formed, while the region where the n-type thin film transistor TFT is formed is selectively exposed.

[0129] The exposure at the region where the n-type thin film transistor TFT is formed is the above-mentioned half exposure. Accordingly, by developing the photo resist film RE thereafter, the photo resist film RE is formed such that the photo resist film RE has a large film thickness on the channel region and a thin film thickness on the portions disposed at both sides of the channel region. Step 4. (FIG. 6D)

[0130] Using the remaining photo resist film RE as a mask, the metal layer GT which is exposed from the mask is selectively etched so that the insulation film GI is exposed.

[0131] In this case, the exposed insulation film GI has a surface thereof slightly etched and has a film thickness smaller than that of the insulation film below the mask.

[0132] Step 5. (FIG. 6E)

[0133] Further, the ion implantation of the n-type impurity of high concentration is performed in the state that the mask remains. Accordingly, at portions other than the region where the mask is formed, the ion of n-type impurity of high concentration is implanted into the semiconductor layer below the insulation film GI so that the drain and source regions are formed.

[0134] By ashing the remaining photo resist film, the surface of the photo resist film is removed while a portion of the surface is made to remain. That is, the ashing process is performed until the remaining photo resist film currently remaining on the channel region having a large film thickness is made to remain and the remaining photo resist film currently remaining on the portions disposed at both sides of the channel region having a small film thickness is removed.

[0135] Using the remaining photo resist film as a mask, the metal layer which is exposed from the mask is etched to form the gate electrode GT. Accordingly, the insulation film GI is exposed and the surface of the exposed insulation film GI is slightly etched to have a film thickness smaller than a film thickness of the insulation film GI below the mask.

[0136] Step 6. (FIG. 6F)

[0137] Further, the ion implantation of the n-type impurity of low concentration is performed in the state that the mask remains. Accordingly, at portions other than the region where the mask is formed, the p-type impurity of low concentration is implanted into the semiconductor layer AS below the insulation film GI.

[0138] [Other Structure of Thin Film Transistor TFT and Forming Method Thereof]

[0139] In the above-mentioned each thin film transistor TFT, the LDD regions are formed at both sides of the channel region such that the channel region is sandwiched by the LDD regions.

[0140] However, it is needless to say that the LDD regions may be constituted at region sides into which the current flows (for example, the drain region sides).

[0141] Also in this case, as can be explicitly understood from process flow views shown in FIG. 8A to FIG. 8D, the above-mentioned advantageous effect can be obtained by adopting the half exposure in the formation of the gate electrode.

[0142]FIG. 9A and FIG. 9B show subsequent steps which follow the above-mentioned TFT fabricating process. After removing the resist remaining in a channel form, the interlayer insulation film which is made of silicon oxide or the like is formed over the source/drain regions and the gate electrode. Although there is no limitation, it is preferable that a film thickness of the interlayer insulation film is not less than 400 nm. After forming the interlayer insulation film, first of all, dry etching (anisotropic etching) is performed so as to form holes having a depth reaching the midst portion of the interlayer insulation film.

[0143] Then, wet etching (isotropic etching) is performed to grow the holes to the source/drain region to form the contact holes. Accordingly, the inclination of lower portions of the contact holes becomes gentler than the inclination of upper portions of the contact holes. Thereafter, conductive material such as metal is filled in the contact holes by deposition or the like thus establishing the contact with the source/drain regions. Accordingly, it is possible to connect the source/drain regions with video signal lines or pixel electrodes.

[0144] Here, the contact holes are formed by performing dry etching first and then performing wet etching so that the regions where the contact holes are formed can be narrowed compared to a case in which the contact holes are formed only by wet etching. Accordingly, it is possible to increase the numerical aperture in the display region of the liquid crystal display device, while it is possible to enhance the integrity of the thin film transistors TFT with respect to the peripheral region of the liquid crystal display device or a display device other than the liquid crystal display device.

[0145] In the above-mentioned explanation, the holes are formed to a depth which reaches the midst portion of the interlayer insulation film by the first dry etching. However, in the formation of the holes by dry etching, the hole may reach a position around a boundary between the interlayer insulation film and the gate insulation film GI or the middle portion of the gate insulation film. That is, the inclination of the side surfaces of the contact holes is changed at a position around the boundary between the interlayer insulation film and the gate insulation film.

[0146] By performing the formation of the holes using dry etching such that holes reach a position near the source/drain regions, the regions where the contact holes are formed can be further narrowed. However, the control of dry etching becomes strict. Accordingly, it is advantageous to change the proportions of dry etching and wet etching by taking the restriction on the area of the contact regions and the accuracy of dry etching into consideration.

[0147]FIG. 10A and FIG. 10B show the constitution which allows the formation of contact holes using only dry etching. Due to such a constitution, it is possible to further narrow the regions of the contact holes compared to the constitution shown in FIG. 9A and FIG. 9B. However, when the contact holes are formed using only dry etching, the source/drain regions made of polysilicon are also etched by dry etching. Accordingly, before forming the interlayer insulation film, portions of the gate insulation film over the source/drain regions are removed and metal films are formed over the portion other than the removed portions. After forming the metal films, the interlayer insulation film is formed and, thereafter, the interlayer insulation film disposed at the regions where the metal films are formed is removed by dry etching. Accordingly, the metal films form block layers for dry etching so that the source/drain regions are prevented from being etched.

[0148] In the constitution shown in FIG. 11, before performing the above-mentioned series of steps, metal films are formed at portions where contacts of the source/drains are formed. That is, metal films are formed over the substrate, polysilicon films are formed over upper portions of the metal films, and thereafter, the source/drain regions are formed by performing the above-mentioned steps to form the interlayer insulation film. Thereafter, the interlayer insulation film and the gate insulation film on the source/drain regions are etched by dry etching. Here, the polysilicon films on the source/drain regions are simultaneously etched by dry etching and, eventually, the holes are formed in the interlayer insulation film, the gate insulation film and the polysilicon films. In this state, by filling the conductive material such as metal into the contact holes, the source/drain regions are electrically connected with the conductive material in the contact holes through a metal layer formed as a layer disposed below the polysilicon film.

[0149] In the above-mentioned constitutions shown in FIG. 10A, FIG. 10B and FIG. 11, it is necessary to form metal layers on upper surfaces or lower surfaces of the source/drain regions and hence, the number of steps is increased. However, since the contact holes can be formed only by dry etching, the contact regions can be further narrowed.

[0150]FIG. 12A to FIG. 12G show another embodiment in which the contact holes of the source/drains are formed only by dry etching. The LDD structures are formed by forming side walls on side surfaces of the gate electrode, and thereafter, a metal film and an interlayer insulation film are formed over the source/drain regions and the gate electrode, and then, the interlayer insulation film is etched by dry etching thus establishing the contact with the source/drain regions.

[0151] In such a constitution, the metal film which constitutes an etching stop layer is formed over the source/drain regions, so that polysilicon which forms the source/drain regions can be prevented from being etched.

[0152] In applying this technical concept to the fabricating method of thin film transistor which has been explained in conjunction with FIG. 4A to FIG. 4E, at the time of removing the gate electrodes other than the channel region by etching to implant the ions of low concentration, the gate insulation film over the region to which the ions of high concentration have been implanted is also removed. Thereafter, after implanting the ions of low concentration, a metal film is formed over the source/drain regions and the gate electrode. Then, an interlayer insulation film is formed over the whole surface of the source/drain electrode and contact holes are formed by dry etching.

[0153] In such a constitution, since the metal film is formed over the source/drain regions, there is no possibility that the polysilicon of the source/drain regions is also etched by dry etching. Here, however, it is necessary to deposit the metal film with a thickness which can prevent the short-circuiting of the gate electrode and the source/drain regions through the metal film. Further, at the time of implanting ions of low concentration, since the gate insulation film which constitutes a through film is not present over the source/drain regions, there still remains the possibility that the impurity is also introduced into the polysilicon. Accordingly, provided that the gate electrode and the source/drain regions are not short-circuited to each other and the possibility of introduction of the impurity to the polysilicon is or is allowed to be low, by adopting this constitution, the steps can be simplified and, at the same time, the contact regions can be narrowed. It is needless to say that the above-mentioned constitution is applicable to the constitutions shown in FIG. 5A to FIG. 5D, FIG. 6A to FIG. 6F and FIG. 8A to FIG. 8D.

[0154]FIG. 6A to FIG. 6F show steps in which the gate electrodes of the p-type thin film transistor and the n-type thin film transistor are formed firstly, and then, the source/drain regions of the p-type thin film transistor are formed, and then n-type thin film transistor is formed. However, the present invention is not limited to such steps. For example, it may be possible to adopt steps in which at the time of firstly forming the gate electrode of the n-type thin film transistor having the LDD structures, the gate electrode of the p-type thin film transistor is simultaneously formed and, thereafter, the p-type thin film transistor may be formed by masking the n-type thin film transistor portion in which the source/drain regions are formed by the ion implantation. In this case, although phosphorus is also implanted into the regions which constitute the source/drain regions of the p-type thin film transistor, by masking the n-type thin film transistor after forming the n-type thin film transistor and implanting boron into the source/drain region of the p-type thin film transistor by an amount twice as much as an amount of phosphorus, the p-type thin film transistor can be realized. Here, although the order of forming the n-type thin film transistor and the p-type thin film transistor may be reversed, since the source/drains implanted with boron larger than phosphorus in quantity is liable to be activated, it is preferable to form the p-type thin film transistor after forming the n-type thin film transistor.

[0155] In the above-mentioned explanation of the half exposure, although the light shielding film formed over the photo mask is formed in a mesh shape, the shape of the light shielding film is not specifically limited. Accordingly, the light shielding film in a stripe shape may be used and any constitution is applicable so long as the light shielding film constitutes a photo mask which can form portions which are exposed to an intermediate level between the completely exposed level and the completely non-exposed level.

[0156] Further, in the above-mentioned fabricating steps of the thin film transistor, there has been disclosed a case in which after forming the regions which are implanted with the ions of high concentration in the source/drain regions, the resist having a large film thickness is made to remain over the channel forming region, and the resist films of a small film thickness disposed at sides of the channel forming region are subjected to the ashing process. However, it may be possible to implant the ions after performing the ashing process. In this case, since the resist is subjected to the ashing process before the resist is hardened by the ion implantation, it is possible to enhance the accuracy of the retraction of the resist.

[0157] With respect to the above-mentioned explanation of steps shown in FIG. 5A to FIG. 5D, the following explanation may conform to the drawings more precisely. That is, the ions of high concentration is implanted in the state shown in FIG. 5B, and thereafter, the resist is subjected to the ashing process such that the width of the resist becomes the width of the channel region of the thin film transistor as shown in FIG. 5C, the metal film is etched using the remaining resist as a mask, and the ions of low concentration are implanted after the metal film is etched as shown in FIG. 5D. It is needless to say that the order of the implantation of the ions of high concentration and the ashing of the resist which allows the channel region to remain can be reversed.

[0158] Heretofore, although the invention has been explained in this specification based on the thin film transistor of the general liquid crystal display device having the constitution in which the pixel electrodes are formed over one substrate and the counter electrode is formed over the other substrate, the present invention is also applicable to a thin film transistor of a liquid crystal display device of a transverse electric field type (IPS) which forms pixel electrodes and a counter electrode in one substrate and drives liquid crystal in the direction parallel to the substrate. It is needless to say that the present invention is also applicable to a thin film transistor adopted by an organic EL display device or the like which uses electro-luminescence. Further, in the above-mentioned display device, it is possible to apply the present invention to only one group of thin film transistors out of a group of thin film transistors provided to the display region and a group of thin film transistors provided to the peripheral region around the display region. Further, although in the above-mentioned explanation the display device in which the peripheral circuit region is constituted of the complementary thin film transistors and the pixel regions are constituted of single-conductive-type thin film transistors, the present invention is not specifically limited to such a display device. That is, the present invention is applicable to a display device in which a peripheral region thereof is constituted of only either p-type or n-type thin film transistors. Further, the present invention is applicable to a display device in which a display region thereof is constituted of p-type and n-type conductive thin film transistors.

[0159] As can be clearly understood from the above-mentioned explanation, according to the display device of the present invention, the numerical aperture can be enhanced and the drawbacks which may be caused by the stepped portions formed in the periphery of the gate electrode of the thin film transistor can be solved.

[0160] Further, according to the fabricating method of the display device of the present invention, the voltage for performing the ion implantation of impurity at the time of forming the thin film transistor can be reduced. 

What is claimed is:
 1. A display device being characterized in that a thin film transistor is formed over a substrate which constitutes the display device, the thin film transistor comprises: a semiconductor layer made of polysilicon which is comprised of a channel region, drain and source regions which are arranged at both sides of the channel region and are doped with impurity of high concentration, and at least one LDD region which is arranged between the drain region and the channel region and between the source region and the channel region or between the drain region and the channel region and are doped with impurity of low concentration, an insulation film which is formed over an upper surface of the semiconductor layer and sequentially decreases a film thickness thereof in a step-like manner as the insulation film is extended to the channel region, the LDD region, the drain and the source region or the drain region respectively, and a gate electrode which is formed over the channel region through the insulation film.
 2. A display device according to claim 1, wherein the insulation film formed over the drain and source regions has a film thickness of not more than 80 nm.
 3. A display device according to claim 1, wherein the insulation film over the LDD region has a film thickness of not more than 90 nm.
 4. A display device according to claim 1, wherein the insulation film over the channel region has a film thickness of not more than 100 nm.
 5. A display device according to claim 1, wherein a film thickness of the insulation film right over the drain and source regions is thinner than a film thickness of the insulation film on the channel region by not less than 20 nm.
 6. A display device according to claim 1, wherein the difference between a film thickness of the insulation film right above the LDD region and a film thickness of the insulation film right above the drain and source regions is larger than the difference between a film thickness of the insulation film right above the channel region and a film thickness of the insulation film right above the LDD region.
 7. A display device being characterized in that the display device comprises: a semiconductor layer made of polysilicon which includes a channel region and drain and source regions arranged at both sides of the channel region which are formed over an insulation substrate, and an insulation film formed over the drain and source regions and having a contact hole, wherein with respect to an angle of a side surface of the contact hole, the angle at a region remote from the drain and source regions is set larger than the angle at a region close to the drain and source regions.
 8. A display device according to claim 7, wherein a portion having a large angle of the side surface of the contact hole is formed by isotropic etching and a portion having a small angle of the side surface of the contact hole is formed by isotropic etching after anisotropic etching.
 9. A display device being characterized in that the display device comprises: a thin film transistor made of polysilicon which includes a gate electrode, a channel region and drain and source regions arranged at both sides of the channel region which are formed over an insulation substrate, a metal film formed over the drain and source regions and the gate electrode, and an insulation film formed over the metal film and having a contact hole, wherein the contact hole is formed by anisotropic etching.
 10. A method for fabricating a display device being characterized in that a thin film transistor is formed over an insulation substrate, and the thin film transistor is formed through steps comprising a step in which a semiconductor layer made of polysilicon, an insulation film and a conductive layer are formed at the substrate side, a step which makes the conductive layer remained on a channel region and an LDD region and performs the ion plantation of impurity of high concentration using the remaining conductive layer as a mask, and a step which makes the conductive layer remained on the channel region and performs the ion plantation of impurity of low concentration using the remaining conductive layer as a mask, and a resist film used for patterning the conductive layer to be remained on the channel region is formed of a portion obtained by removing a periphery of the resist film used for patterning the conductive layer remained on the channel region and the LDD region, and at the time of making the conductive film remained on the channel region and the LDD region, and further on the channel region, by using the conductive film as a mask, a surface of the insulation film which is exposed from the mask is slightly etched.
 11. A method for fabricating a display device according to claim 10, wherein the resist film to be remained on the channel region and the LDD regions has a large film thickness over the channel region and a small film thickness over the LDD regions, and the resist film to be remained on the channel region is formed by ashing the resist film remained on the channel region and the LDD regions. 